1100 Aluminium Angles, Channels & Extrusions
1100 Aluminium Angles, Channels & Extrusions
Aluminium Alloy 1100 Angles & Channels Supplier in India
Aluminium Alloy ASTM B211 Angles, Channels & Extrusions, Aluminium Alloy 1100 Extrusions
JAGDISH METAL is a leading Suppliers & Manufacturer of Aluminium Alloy 1100 Angles & Channels, Aluminium Alloy 1100 Angles, Channels & Extrusions, Aluminium Alloy UNS A91100 Extrusions , Aluminium Alloy ASTM B211 Angles, Channels & , Aluminium Alloy ASTM B-209M Angles / Channels / Extrusions.
These 1100 Aluminium Alloy Angles / Channels / Extrusions are made by surpassing Aluminium between moves underneath weight, it gets to be more slender and more in the moving heading.The Aluminium Alloy 1100 Angles / Channels / Extrusions are accessible in assortment of sizes and thickness.Aluminium 1100 is among the gentlest Aluminium composites and therefore isn't utilized for high-quality or high-weight applications.
Specification Of Aluminium Alloy 1100 Angles, Channels & Extrusions:
| Standards | : | ASTM B221, ASTM-B-209M, EN573, EN485, AMS 4003 |
| Grade | : | Aluminium Alloy 1100 (UNS A91100) |
| Thickness | : | 0.9mm - 7mm |
| Finish | : | Mill, Customer specific finish |
| Length | : | Coating 6.5 meters, Anodizing 6.5 meters, Mill finish 5 meters. |
| Surface | : | Anodize, electrophoresis, powder coating, PVDF coating, wood grain painting, matted, etc |
Chemical Composition Of Aluminium Alloy 1100 Angles, Channels & Extrusions:
| Alloy | Fe | Si | Mg | Mn | Cu | Zn | Ti | Cr | Each | AI |
|---|---|---|---|---|---|---|---|---|---|---|
| 1100 (min) | 0.35 | 0.25 | 0.01 | 0.01 | 0.05 | 0.01 | 0.020 | Trace | 0.05 | 99.60% |
| 1100 (max) | 0.50 | 0.35 | 0.03 | 0.05 | 0.20 | 0.05 | 0.030 | Trace | 0.15 | remainder |
Mechanical Properties of Aluminium 1100 Angles, Channels & Extrusions:
| Alloy | Temper | UTS(Mpa) | % Elongation | |||
| Min | Max | 0.5 mm -0.8 mm | 0.81 mm - 1.30 mm | 1.30 mm - above | ||
| 1100 | O | 75 | 110 | 20 | 25 | 29 |
| H12 | 95 | 130 | 5 | 6 | 7 | |
| H14 | 110 | 145 | 3 | 4 | 5 | |
| H16 | 130 | 165 | 2 | 3 | 4 | |
| H18 | 150 | --- | 2 | 2 | 3 | |